@article{20851,
  abstract     = {High-voltage disordered spinel LiNi0.5Mn1.5O4 is a promising cathode material for high power density in lithium-ion batteries. However, it suffers from poor cycle life associated with the rock-salt phase transformation. This study presents a straightforward synthesis approach to enhance the electrochemical performance of LiNi0.5Mn1.5O4 through a synergistic solid-state modification with LiF and AlF3. This dual modification promotes rapid Li⁺ diffusion, enables near-complete delithiation/lithiation, approaching the theoretical capacity of disordered LiNi0.5Mn1.5O4, and, more importantly, effectively mitigates the formation of the rock-salt phase, thereby enhancing structural stability, as confirmed by operando X-ray absorption spectroscopy (XAS) and synchrotron X-ray diffraction (SXRD). As a result, the optimized LiNi0.5Mn1.5O4 (10 mg AlF3 + 30 mg LiF) delivers high reversible capacities of 142.1, 139.1, 129.2, 121.6, 110.3, 93.5, and 76.1 mAh∙g−1 at 0.2C, 0.5C, 1.0C, 2.0C, 3.0C, 4.0C, and 5.0C, respectively. Full cells using graphite as the anode and a high-loading cathode exhibit excellent cycling performance. They retain 80% of their capacity after 200 cycles at 0.5C within a voltage window of 3.5–4.9 V with cathode loading of 11 mg∙cm−2. The findings of this study will significantly advance high-power LiNi0.5Mn1.5O4 materials, offering improved battery life and thereby enhancing their potential for practical applications.},
  author       = {Chang, Xingqi and Escudero, Carlos and Black, Ashley P. and Horta, Sharona and Martínez, Elías and Lu, Xuan and Llorca, Jordi and Ibáñez, Maria and Biendicho, Jordi Jacas and Cabot, Andreu},
  issn         = {2198-3844},
  journal      = {Advanced Science},
  keywords     = {disordered spinel LiNi0.5Mn1.5O4 (LNMO), generation 3b batteries, operando SXRD, operando XAS, rock-salt, solid-state synthesis},
  number       = {11},
  publisher    = {Wiley},
  title        = {{Mitigating the rock-salt phase transformation in disordered LNMO through synergetic solid-state AlF3/LiF modifications}},
  doi          = {10.1002/advs.202515962},
  volume       = {13},
  year         = {2026},
}